Hvilke partikelmaterialer understøttes til SpectroCuvette™ S i SpectroWorks™?

SpectroWorks™ understøtter et bredt udvalg af partikelmaterialer til brug med SpectroCuvette™ S. De er alle baseret på publicerede videnskabelige artikler. Denne tabel giver et komplet overblik over alle understøttede materialer og deres kilder.

Partikelmateriale Kilde(r)
Antheraea assamensis Perotto et al. 2017: Fibroin film; n 0.3-1.695 µm
Antheraea mylitta Perotto et al. 2017: Fibroin film; n 0.3-1.695 µm
B4C Larruquert et al. 2012: n,k 0.001738-21.54 µm
Bombyx_mori Bucciarelli et al. 2018: Photocrosslinkable fibroin film, crosslinked; n 0.4-1.5 µm
Bucciarelli et al. 2018: Photocrosslinkable fibroin film, uncrosslinked; n 0.4-1.5 µm
Bucciarelli et al. 2018: Pure fibroin film, formed using formic acid; n 0.4-1.5 µm
Bucciarelli et al. 2018: Pure fibroin film, formed using water; n 0.4-1.5 µm
Bucciarelli et al. 2018: Photocrosslinkable sericin film, crosslinked; n 0.4-1.5 µm
Bucciarelli et al. 2018: Photocrosslinkable sericin film, uncrosslinked; n 0.4-1.5 µm
Bucciarelli et al. 2018: Sericin film; n 0.4-1.5 µm
Perotto et al. 2017: Native fibroin film; n 0.3-1.7 µm
Perotto et al. 2017: Uncrystallized fibroin film; n 0.3-1.7 µm
Perotto et al. 2017: Crystallized fibroin film; n 0.3-1.7 µm
C Larruquert et al. 2013: n,k 0.0197-10.1 µm
Arakawa et al. 1977: n,k 0.326-2.07 µm
Querry 1985: Pyrolytic carbon; n,k 0.21-55.6 µm
Song et al. 2018: c-HOPG; n(e) 0.193-1.69 µm
Song et al. 2018: s-HOPG; n(e) 0.193-1.69 µm
Ermolaev et al. 2020: Carbon nanotubes film, aerosol CVD; n,k 0.250-3.30 µm
Song et al. 2020: Carbon nanotubes film, Arc grown; n,k 0.370-1.69 µm
CaCO3 Ghosh 1999: n(o) 0.204-2.172 µm
Ghosh 1999: n(e) 0.204-2.172 µm
colon Giannios et al. 2016: Mucosa; n,k 0.45-1.551 µm
Giannios et al. 2016: Submucosa; n,k 0.45-1.551 µm
Giannios et al. 2016: Serosa; n,k 0.45-1.551 µm
CsCl Li 1976: n 0.18-40 µm
CuCl Feldman and Horowitz 1969: n 0.43-2.5 µm
Diesel soot Querry 1987: Sample 1; n,k 0.260-55.6 µm
Querry 1987: Sample 1, heated; n,k 0.260-55.6 µm
HfO2 Al-Kuhaili 2004: Thin film; n 0.2-2.0 µm
KCL Li 1976: n 0.18-35 µm
Querry 1987: n,k 0.22-167 µm
LiCl Li 1976: n 0.17-16 µm
Liver Giannios et al. 2016: n,k 0.45-1.551 µm
MgO Stephens and Malitson 1952: n 0.36-5.4 µm
NaCl Querry 1987: n,k 0.22-167 µm
Li 1976: n 0.20-30 µm
Os Nemoshkalenko et al. 1968: n,k(o) 0.24-15 µm
Nemoshkalenko et al. 1968: n,k(e) 0.25-8.0 µm
Polycarbonate Zhang et al. 2020: n,k 0.4-20 µm
Polydimethylsiloxane Gupta et al. 2019: n 0.30-1.69 µm
Polyetherimide Zhang et al. 2020: n,k 0.4-20 µm
Polyethylene terephthalate Zhang et al. 2020: n,k 0.4-20 µm
Polylactic acid Bodurov et al. 2016: PDLA; n 0.405-0.635 µm
Polystyrene Sultanova et al. 2009: n 0.437-1.05 µm
Samia ricini Perotto et al. 2017: Fibroin film; n 0.3-1.695 µm
SiC Singh et al. 1971: α-SiC; n(o) 0.488-1.064 µm
Singh et al. 1971: α-SiC; n(e) 0.488-1.064 µm
Wang et al. 2013: 6H-SiC; n(o) 0.436-2.33 µm
Wang et al. 2013: 6H-SiC; n(e) 0.436-2.33 µm
Wang et al. 2013: 4H-SiC; n(o) 0.405-5 µm
Wang et al. 2013: 4H-SiC; n(e) 0.405-2.33 µm
Larruquert et al. 2011: Thin film; n,k 0.006154-131.7 µm
TeO2 Uchida 1971: α-TeO2; n(o) 0.4-1.0 µm
Uchida 1971: α-TeO2; n(e) 0.4-1.0 µm
TiO2 Devore 1951: Crystal; n(o) 0.43-1.53 µm
Devore 1951: Crystal; n(e) 0.43-1.53 µm
Sarkar et al. 2019: Thin film; n,k 0.30-1.69 µm
Siefke et al. 2016: Thin film; n,k 0.120-125 µm
WO3 Kulikova et al. 2020: n,k 0.3-1.0 µm
Y2O3 Nigara 1968: n 0.25-9.6 µm
ZnO Bond et al. 1965: n(o) 0.45-4.0 µm
Bond et al. 1965: n(e) 0.45-4.0 µm
Stelling et al. 2017: n,k 0.302-1.685 µm
Aguilar et al. 2019: n,k 0.3-3.2 µm; 100% ZnO
Querry 1985: n,k 0.21-55.6 µm
ZnO-CdO Aguilar et al. 2019: n,k 0.3-3.2 µm; 100% ZnO
ZrO2 Wood and Nassau 1982: 12 mol % Y2O3; n 0.361-5.135 µm
ZrO2-Y2O3

Wood and Nassau 1982: 12 mol % Y2O3; n 0.361-5.135 µm